S. R. Bakhshi, M. Salehi, H. Edris, G. H. Borhani. Isothermal oxidation behavior of plasma-sprayed Mo-Si-B intermetallic coatings on plain steel. Journal of Advanced Materials in Engineering (Esteghlal) 2010; 29 (1) :21-30
URL: http://jame.iut.ac.ir/article-1-508-en.html
URL: http://jame.iut.ac.ir/article-1-508-en.html
Department of Materials Engineering, Malek-Ashtar University of Technology , bakhshisr@ma.iut.ac.ir
Abstract: (8368 Views)
In this study, Mo-14Si-10B and Mo-57Si-10B (at%) elemental powders were separately milled using an attritor mill. Mechanically alloyed powders were agglomerated and annealed. Then, powders of Mo-Si-B as alloyed (with composites) and agglomerated (without composites) were plasma sprayed onto plain carbon steels. The samples, both coated and non-coated, were subjected to isothermal oxidation tests. Metallurgical characteristics of powders and coatings were evaluated by SEM and XRD. Plasma-sprayed Mo-Si-B coatings (with phases of MoSi2, Mo5Si3, MoB and Mo5SiB2) greatly improved the oxidation resistance of the plain steel substrates, but plasma-sprayed Mo-Si-B coatings (without any phases) did not significantly improve the oxidation rate of substrates. Also, the kinetics and composition of the oxide-scale have been found to depend on the alloy composition.
Keywords: Mechanical alloying, Thermal spraying, High temperature oxidation, Molybdenum silicides, Mo-Si-B.
Type of Study: Research |
Subject:
General
Received: 2015/02/9 | Accepted: 2015/05/5 | Published: 2015/05/5
Received: 2015/02/9 | Accepted: 2015/05/5 | Published: 2015/05/5
Send email to the article author