A. Maghzian, A. Monshi, M.H. Fathi. Synthesis and Characterization of Nano-structured CaTiO3 Coating via Sol-gel Dip-coating Route. Journal of Advanced Materials in Engineering (Esteghlal) 2010; 29 (2) :13-22
URL: http://jame.iut.ac.ir/article-1-513-en.html
URL: http://jame.iut.ac.ir/article-1-513-en.html
Department of Materials Engineering, Isfahan University of Technology , a.maghzian@gmail.com
Abstract: (8689 Views)
In the last decade, Calcium Titanate has been introduced as a bioceramic with acceptable mechanical and biological properties for orthopaedic implant applications. In this study, CaTiO3 nano-structure coating was produced by sol-gel dip-coating route for biomedical applications. Calcium nitrate and titanium isopropoxide were used as a precursor. After coating process, the specimen was subjected to rapid thermal annealing (RTA) at 800°C. The phase structure, functional groups and surface morphology of coating were investigated by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR) and scanning electron microscopy (SEM). Uniform crack-free nano-structured coatings were obtained with perovskite crystal structure.
Keywords: Dip-coating, Nano-structured coatings, Rapid thermal annealing, CaTiO3 Coating, Orthopaedic implants.
Type of Study: Research |
Subject:
General
Received: 2015/02/9 | Accepted: 2015/05/5 | Published: 2015/05/5
Received: 2015/02/9 | Accepted: 2015/05/5 | Published: 2015/05/5
Send email to the article author