Journal of Advanced Materials in Engineering (Esteghlal)

Nanoparticles of Mg–Co–Ti substituted strontium hexaferrite with nominal composition of SrFe_12-2x(Mg,Co)_0.5x Ti_xO₁₉ (x=0-2.5) were synthesized by a co-precipitation method. The structural, magnetic and electromagnetic properties of samples were studied as a function of x by thermal gravimetric (TG), X-ray diffraction (XRD), transmission electron microscopy (TEM), vibrating sample magnetometer (VSM) and vector network analysis. It was found that the synthesis temperature increases with an increase in Mg–Co–Ti substitution and hence the particle size decreases. The XRD results showed that whole samples had good crystallinity and with an increase incations, the impurity phase of Fe₂O₃ appears. The results of hysteresis loops indicated that the saturation of magnetization of ferrite decreases from 40 emu/g to 19 emu/g with an increase in x. The Mössbauer spectroscopy showed that the cations are substituted in the 12k site of magnetoplumbite structure. Vector network measurements showed that the doped samples had much more effective reflection loss values than those of undoped ferrites. As a result, Mg–Co–Ti doped Sr-hexaferrites with x=2 can be proposed as suitable absorbers for applications in microwave technology with a good deal of consistency.