Hassani B, Karimzadeh F, Enayati M, Borouni M. Effects of Friction Stir Processing and T6 Heat Treatment on Wear Properties of Weld Metal of Cast AZ91C Alloy . Journal of Advanced Materials in Engineering (Esteghlal) 2016; 35 (1) :99-107
URL: http://jame.iut.ac.ir/article-1-789-en.html
URL: http://jame.iut.ac.ir/article-1-789-en.html
1- Department of Materials Engineering, Isfahan University of Technology, Isfahan, Iran , bh_metal84@yahoo.com
Abstract: (9520 Views)
In this study, TIG welding was used to clad and repair the surface of cast AZ91C magnesium alloy. Then, friction stir processing and T6 heat treatment wrer applied on the welded region. Microhardness results showed an improvement in the mean hardness of welded zone and also FSPed zone. Increase in the mean microhardness of the welded zone after T6 heat treatment to the maximum value was also concluded. The results of wear test showed that the wear resistance of the welded area was improved. Further improvement in wear properties was obtained after friction stir processing and T6 heat treatment.
Type of Study: Research |
Subject:
General
Received: 2016/06/14 | Accepted: 2016/06/14 | Published: 2016/06/14
Received: 2016/06/14 | Accepted: 2016/06/14 | Published: 2016/06/14
Send email to the article author