Showing 2 results for F. Shahriari
A. Azimi Dastgerdi, F. Ashrafizadeh, M. R. Toroghinejad, F. Shahriari , H. Zahraei,
Volume 30, Issue 2 (Dec 2011)
Abstract
In this paper, bare spot defects in hot-dip galvanized sheets were studied in terms of the microstructure and their influence on the corrosion and mechanical properties. Surface characteristics and microstructural features were examined by scanning electron microscopy equipped with energy dispersive spectroscopy microanalysis system. The results showed that the major cause of the bare spots was the lack of wetability of the sheet surface due to contamination, improper heat treatment or chemical composition. Corrosion resistance was evaluated by standard salt spray test. Mechanical properties were examined by tensile testing. The time to red rust was much shorter on the bare spots as compared to other regions, but it appeared that bare spot defects had no significant effect on the mechanical properties of the galvanized steel sheets.
F. Shahriari, F. Ashrafizadeh, A. Saatchi,
Volume 31, Issue 2 (Dec 2012)
Abstract
Although titanium has been recognized for its excellent bio-compatibility with human tissues and good corrosion resistance in some specific environments, little attention has been paid to the surface enrichment of the components by titanium. In this paper, titanium diffusion coating was formed on the surface of Ni-based alloy B-1900 via pack cementation technique and the microstructure of the coatings obtained was studied. Diffusion titanizing was carried out via pack cementation technique at 850 and 950 C for 3 hours in a mixture of commercially pure titanium, Al2O3 and NH4Cl powder. Microstructure, phase composition and concentration profile of the coatings were examined using optical and electron metallography, X-ray diffraction, and glow discharge optical spectroscopy. The results showed that Ti2Ni and AlNi2Ti were the main constituents of the coating. The formation mechanism of the coatings was also evaluated.