Showing 3 results for M.H. Abbasi
Kh. Biralvand, M.h. Abbasi, A. Saidi,
Volume 31, Issue 1 (Jun 2012)
Abstract
Carbothermic reduction of Molybdenite in the presence of Magnesium oxide was thermodynamically studied. The stability diagrams for MoS2-MgO and MoS2-MgO-C Systems was prepared. The reduction of MoS2 with Carbon in the presence of Magnesium oxide proceeded through the direct oxidation of MoS2 by MgO to form intermediate molybdenum oxidized Species, MoO2 and MgMoO4. The results showed that the gaseous phase is mainly composed of CO. Stability diagrams for Mo-O-C (Reduction of MoO2 with carbon) and Mo-Mg-C-S-O (Reduction of MgMoO4 with carbon) were also investigated. The results showed that the Reduction of oxidized species leads to the formation of Mo, Mo2C, MoC or MgO products.
K. Sheybani, M.h. Abbasi, M. Shamanian ,
Volume 33, Issue 2 (Journal of Advanced Materials-fall 2015)
Abstract
in this research, the kinetics of carbothermic reduction of molybdenite in the presence of sodium carbonate was studied. For this purpose, mixed powder of molybdenite, graphite, and sodium carbonate with 1:4:2 mole ratio was investigated using simultaneous thermal analysis (STA) at the heating rates of 10, 15 and 20 0C /min. The results of thermal analysis were evaluated through Friedman, Kissinger, Ozawa and Coats-Redfern methods. The activation energy of reduction reaction was determined 220 kj/mole, and it was found that the reaction was chemically controlled. To study the reaction mechanism, the mixed powder was heated to 400, 800 and 1100 0C in argon atmosphere at the heating rate of 10 0C/min. X- Ray diffraction
of the reaction products and thermodynamic analysis at these temperatures indicated that carbothermic reduction of molybdenite in the presence of sodium carbonate would advance through the formation of intermediate phases, Na2MoO4 and MoO2