S. Bassaki, F. Golestani Fard, R. Naghizadeh, M. Rashidzadeh,
Volume 34, Issue 3 (Journal of Advanced Materials-fall 2015)
Abstract
Titanium dioxide-nickel oxide porous coatings were synthesized by Plasma Electrolytic Oxidation (PEO)/ ElectroPhoretic Deposition (EPD) in one step and within a short time. The main purpose of this research was to increase photocatalytic activity of titanium oxide by increasing surface area and coupling of titanium oxide with nickel oxide. Applied voltage effects on phase structure, surface morphology and photocatalytic efficiency of coatings were studied. Phase structure and surface morphology of the synthesized catalysts were investigated by XRD and SEM, respectively. Photocatalytic efficiency of the samples was studied through measuring the decomposition rate of 4-chlorophenol. The results showed that the coatings mainly consisted of anatase and nickel oxide phases whose amounts in coatings increased with the voltage. There was an enhancement of the photocatalytic efficiency in TiO2/NiO composite coatings compared with TiO2 coatings. Besides, there was an optimum amount of NiO to reach maximum photocatalytic efficiently.
H. Saki, M. Morakabati, R. Mahdavi,
Volume 40, Issue 3 (Journal of Advanced Materials-Fall 2021)
Abstract
Metastable beta titanium alloys have the ability to achieve different microstructures as a result of various heat treatment cycles. The aim of the present study was to create a combination of fine spherical and needle-shaped alpha phase in a metastable beta Titanium alloy (Ti-3Al-8Mo-7V-3Cr) using two-phase solution annealing and aging to improve tensile properties. In this regard, one strip of the alloy was solution annealed in the two-phase region (α+β) at 750°C. Then, some of the solution treated specimens were aged in one step and the others in two steps. The microstructural observation and phase analysis were studied by scanning electron microscope (SEM) and X-ray diffraction (XRD), respectively followed by investigating tensile properties using tensile test. The results exhibited that the microstructure of the alloy after annealing in the two-phase region (α+β) consisted of a spherical primary alpha phase of 1 μm in the beta matrix. One-step aging at 600°C resulted in a microstructure without secondary alpha layers. This heat treatment cycle resulted a yield strength of 980 MPa and fracture strain of 13.9%. Two-step aging at 300°C and 600°C led to formation of the secondary alpha layers with 0.1 μm thickness and increased the yield strength and fracture strain to 1007 MPa and 15.8%, respectively.