Showing 306 results for Co
S. N. Hosseini, F. Karimzadeh, M. H. Enayati,
Volume 39, Issue 4 (2-2021)
Abstract
The bare and pre-oxidized AISI 430 pieces were screen printed by copper ferrite spinel coatings. Good bonding between the coating and the substrate was achieved by the reactive sintering process of the reduced coating. The energy dispersive X-ray spectroscopy (EDS) analysis revealed that the scale is a double layer consisting of a chromia-rich subscale and an outer Cu/Fe-rich spinel. The results showed that the spinel protection layer not only significantly decreased the area specific resistance (ASR), but also inhibited the subscale growth by acting as a barrier to the inward diffusion of oxygen. ASRs of 19.7 and 32.5 mΩ.cm2, much lower than that of the bare substrate (153.4 mΩ.cm2), at 800 °C after 400 h oxidation were achieved for the bare and pre-oxidized copper ferrite spinel coated samples, respectively. Excellent, stable ASR (20.5 mΩ.cm2) was obtained with copper ferrite coating after 600 h of exposure at 800 °C. The high electrical conductivity of CuFe2O4 and its doping by Mn, the growth reduction of Cr2O3 oxide scale and the good coating to substrate adherence are proposed to be responsible for substantial improvement in electrical conductivity.
S. Masoomi Ganjgah , M. Abbasi,
Volume 39, Issue 4 (2-2021)
Abstract
This study aims at investigating changes in microstructure and strength of W alloy and Cu bimetals with varying spark plasma sintering (SPS) temperature and percentage of copper in W-Cu-Ni alloy. After SPS of W (12 wt%)-Cu (14 wt%)-Ni (3 wt%) alloy powder into consolidated discs at 1350 ° C, they were spark plasma sintered to copper discs at various temperatures. Assessment of the interface microstructure and shear strength was performed by field emission scanning electron microscpe (FESEM) and shear strength test, respectively. Results indicated SPS is successful in forming a perfect metallic bond with monolithic interface and high shear strength of about 45 MPa in Cu/W-12Cu-3Ni bimetal that is extra high quality and not reported in previous investigations.
S. Arjmand, G. H. Akbari, G. R. Khayati,
Volume 39, Issue 4 (2-2021)
Abstract
The purpose of the present work is to investigate the influence of the number of weld-passes on microstructure, hardness and residual stresses of composite coatings composed of Ti-Al-Si intermetallic compounds. In this regard, surface coating of pure Ti was carried out using one and two passes of tungsten inert gas (TIG) welding with an Al filler alloy (grade 4043). Phase and structural evaluations of the coatings were investigated by X-ray diffraction, optical and scanning electron microscopies. microhardness and residual stress values of the coatings were measured using ASTM E384-HV device and the Sin2ψ method, respectively. The results showed that as the number of welding passes increased or the dilution ratio decreased, the volume fraction of Ti5Si3-Al3Ti intermetallic phases within the fusion zone increased and the volume fraction of martensite phase in the heat affected zone decreased. As a result, the average hardness value of the coating increased to be about 130 % compared to that of the pure Ti substrate. The tensile residual stresses at the center line of fusion zone were 165 ± 30 and 210 ± 35 MPa for the coatings prepared in one and two welding passes, respectively.
N. Zakeri, H.r. Rezaie, J. Javadpour, M. Kharaziha,
Volume 39, Issue 4 (2-2021)
Abstract
In recent years, nanoceramics have been used in scaffolds to emulate the nanocomposite with a three-dimensional structure of natural bone tissue. In this regard, polycaprolactone biopolymer is widely used as a scaffold in bone tissue engineering. The goal of this research is to produce porous scaffolds of polycaprolactone - zeolite biocomposite with suitable mechanical, bioactive and biological properties for bone tissue engineering applications. The nanocomposite scaffolds were synthesized by solvent casting/particulate leaching and freeze-drying approaches. Microscopic investigations showed generation of pores with an average size of 200-400μm after addition of ceramic phase. Energy dispersive X-ray analysis confirmed uniform distribution of ceramic phase in polycaprolactone matrix. FTIR results determined the binding type of zeolite nanoparticles to the polycaprolactone matrix as physical bonding. The results of mechanical tests showed the increase in young’s modulus after addition of ceramic phase (from 0.04 to 0.3 and 3 to 7 MPa, respectively). The hydrophilicity of polycaprolactone increased after adding nanozeolite and more weight loss was observed for scaffold containing 20% zeolite (53.52 6 1.6%) with an increase in the rate of hydroxyapatite formation. The results showed that the prepared scaffolds have potential for cancellous bone tissue engineering application.
I. Forooghi , M. Mashhadi,
Volume 39, Issue 4 (2-2021)
Abstract
Due to their unique features, Ultra-High Temperature Ceramics (UHTCs) have potential applications in aerospace, military and industry. ZrB2-SiC composite as one of these ceramics has been at the center of researches due to its attractive mechanical, thermal and oxidation resistance. In this study, the effect of ZrC addition on pressureless sintering behavior, mechanical, microstructural and thermal properties of ZrB2-SiC nanocomposite were investigated. For this purpose, micron-sized ZrB2 and ZrC powders and nano-sized SiC powder were used. ZrB2-20vol% SiC nanocomposites with addition of (3, 6, 9, 12, 15) vol% ZrC were sintered by pressureless sintering method at 2100 ºC. The results showed that the addition of ZrC improved relative density, hardness and fracture toughness of ZrB2-20vol% SiC nanocomposite. Optimum properties were obtained in a sample containing 12 vol% ZrC and the relative density, hardness and fracture toughness of this sample were reported to be 99.01%, 16.95 Gpa and 5.43 Mpa.m0.5, respectively. Thermal analysis of the samples showed that by adding ZrC, thermal diffusivity of this nanocomposite reduced. The highest thermal diffusivity at room temperature equaled 35.3 mm2 /s and was obtained for ZS composite.
Kh. Zamani, M. Tavoosi, A. Ghasemi ,
Volume 39, Issue 4 (2-2021)
Abstract
In this research, effect of B and Si addition on the structural and magnetic properties of AlCoCrMnNi high-entropy alloys was investigated. The structural and magnetic properties of AlCoCrMnNiX(X= B, Si) alloys were studied by X-ray diffractometer (XRD), scanning electron microscopy (SEM), differential scanning calorimetry (DSC) and vibrating sample magnetometer (VSM). First, the constituent components of the AlCoCrMnNiX (X=B, Si) alloys were mixed for 10 hours. XRD analysis revealed that the solid solution was not formed by mixing. The alloys were then annealed at 900 ˚C for 10 hours. XRD results revealed formation of a solid solution with BCC structure in AlCoCrMnNi and AlCoCrMnNiB alloys. For AlCoCrMnNiSi and AlCoCrMnNiSiB alloys, Ni2Si and Cr2Si3 intermetallics were formed in addition to the solid solution with BCC structure. VSM results suggested that while forming the solid solution for AlCoCrMnNi alloy, soft magnetic properties improved so that magnetic saturation and coercivity increased from 40.22 to 64.46 emu/g, and from 180.143 to 14.09 Oe, respectively.
S. Borhani Esfahani, H. R. Salimi Jazi, M. H. Fathi, A. Ershad Langroudi, M. Khoshnam,
Volume 40, Issue 1 (5-2021)
Abstract
In this research, a kind of environmentally-friendly inorganic-organic hybrid nanocomposite coating based on silica containing titania/silica core/shell nanoparticles was synthesized and characterized for conservation of facade tiles in historical buildings. The matrix of the composite was prepared by sol-gel process via two methods of ultrasonic and reflux stirring. Tetraethyl orthosilicate (TEOS) and poly-dimethyl siloxane hydroxy-terminated (PDMS-OH) were used for the formation of silica network and creation of flexibility and hydrophobicity, respectively. Titania nanoparticles were used in the form of titania/silica core/shell as ultraviolet absorber. The synthesized nanocomposite was applied on the microscope slides and tiles by dip coating technique. The properties of nanoparticles and coatings were characterized by Fourier-transform infrared spectroscopy (FTIR), Transmission electron microscopy (TEM) and water contact angle measurement. The results revealed that formation of titania/silica core/shell structure was successful. The investigation of PDMS content effect on transparency, cohesion and hydrophobicity of the coating confirmed that the optimum content of this siloxane was around 20 wt.%. In general, the results showed that the silica-based hybrid nanocomposite reinforced with TiO2/SiO2 core/shell nanoparticles could produce a transparent and hydrophobic coating for tile and glass protection.
H. R. Karimi, H. Mansouri, M. R. Loghman Estarki, M. Tavoosi , H. Jamali,
Volume 40, Issue 1 (5-2021)
Abstract
This study aimed to compare the phase changes and morphology of yttria-stabilized zirconium oxide powders (YSZ) synthesized by co-precipitation and molten salt methods. Ammonia precipitating agent was used for the synthesis of YSZ powder by co-precipitation method and a mixture of sodium carbonate and potassium carbonate salts was used as a molten salt in the molten salt method. Samples were characterized by X-Ray Diffraction (XRD), Field Emission Scanning Electron Microscopy (FESEM), Fourier Transform Infrared Spectroscopy (FTIR), Thermal Gravimetric Analysis (TGA), and Differential Scanning Calorimetry (DSC) analysis. The results showed that only the sample prepared with zirconium oxychloride and yttrium nitrate by co-precipitation method had a single phase of yttria-stabilized zirconium oxide with tetragonal crystal lattice and particle size distribution in the range of 30 to 55 nm. The powder synthesized by the molten salt method contained a mixture of zirconia with monoclinic crystal lattice and yttria stabilized zirconia with tetragonal crystal lattice and particle size of 200 nm.
R. Amirarsalani, M. Morakabati, R. Mahdavi,
Volume 40, Issue 1 (5-2021)
Abstract
In this research, the hot deformation behavior of W360 tool steel was investigated using hot compression test at 1000-1200°C and strain rates of 0.001, 0.01, 0.1, and 1 s-1. According to the results, dynamic recrystallization was found the most important restoration factor of this alloy during hot deformation. Recrystallization was enhanced with an increase in temperature and strain rate. Also, the hot working process was optimized by drawing the processing map of this steel. Microstructural images obtained from the hot compression test showed that recrystallization started at 1000°C and the strain rate of 0.01 s-1 and developed with increasing temperature and strain rate due to an increase in the stored energy and suitable regions for nucleation. The results of drawing the processing map showed that the best hot deformation region was the temperature range of 1050-1150°C and strain rates of 0.1-1 s-1.
M. Khosravi , M. Mansouri, A. Gholami, Y. Yaghoubinezhad,
Volume 40, Issue 1 (5-2021)
Abstract
In this research, the effect of graphene oxide (GO) and reduced graphene oxide (RGO) nanosheets on the mechanical and microstructural properties of AISI 304 stainless steel welded joints produced by the flux-cored arc welding (FCAW) method was investigated. Light microscope, field emission scanning electron microscope (FE-SEM) equipped with energy-dispersive X-ray spectroscopy (EDS), X-ray diffraction analysis (XRD), Raman spectroscopy, and tensile strength test were used to characterize the samples. GO was synthesized by modified Hummers’ method and reduced by hydrazine. Accordingly, the pastes of GO and RGO in different concentrations of 1, 3, and 10 mg/ml were applied in the groove. The results demonstrated that increasing the RGO concentration up to 10 mg/ml improves the tensile strength and hardness values of welded joints up to 23% and 43%, respectively. It seems that RGO nanosheets have a significant effect on the mechanical properties of the welded joints by pinning of dislocations.
S. Shahzamani, M. R. Toroghinejad, A. Asharfi,
Volume 40, Issue 2 (9-2021)
Abstract
In this study, Al/Al2O3 composite was produced by accumulative roll bonding (ARB) process coupled with the plasma electrolytic oxidation (PEO) process. The alumina was grown on Al sheets by electrolyte technique with three different thicknesses (10, 20, and 40 µm). The results showed that incorporation of alumina up to 3.22 vol.% in aluminum matrix enhanced the yield and tensile strength of the composite, whereas increasing the amount of alumina up to 6.25 vol.% deteriorated the tensile properties. In the last part, a serial sectioning process was employed to develop a three-dimensional (3D) representation of the microstructure of Al2O3 particles reinforced Al composite for visualization and finite-element modeling (FEM).
H. Fallah-Arani, S. Baghshahi, A. Sedghi, F. Shahbaz Tehrani,
Volume 40, Issue 2 (9-2021)
Abstract
In this research, the influence of titanium dioxide nanoparticles on the structural and magnetic properties of high-temperature superconductor Bi1.6Pb0.4Sr2Ca2Cu3O10+θ (Bi-2223) from the Bi-based ceramic system (BSCCO) was studied. In order to investigate the synthesized samples, X-ray diffractometry and magnetic measurements were performed. Based on the magnetic measurements, the superconductivity transition temperature declined with the increase in the nanoparticles' content. The addition of nanoparticles affected on the hysteresis loop width. Accordingly, the compound containing 0.2 wt.% nanoparticles had the maximum magnetization, hysteresis loop width, and critical current density.
R. Bagheri, F. Karimzadeh, A. Kermanpur , M. Kharaziha,
Volume 40, Issue 2 (9-2021)
Abstract
A new method has been presented for the synthesis of copper (Cu)/copper oxide (CuO)-nanoparticles (NPs), based on the process of corrosion and oxidation of Cu-NPs on the surface of the gold electrode by nitric acid. Cu-NPs were deposited on the surface using potentiometric method. The high concentration of Cu-NPs was estimated by Differential Pulse Voltammetry (DPV). The process of growth and distribution of CuO-NPs on the surface of Cu-NPs using structural analysis of Fourier Transform Infrared Spectroscopy (FTIR) and X-ray diffraction (XRD) showed that nitrate was well absorbed and a sharp hydroxyl peak appeared and a phase of CuO NPs formed on the electrode surface. The surface morphology indicated that the average size reduced from about 150 nm to 50 nm in the presence of nitrate. This can be due to the oxidation of Cu nanoparticles on the surface and reduction of particle size compared to the absence of nitric acid. This simple and low-cost method can be used as a surface modification of antibacterial and active catalyst electrodes.
M. Salehi, M. Eskandari, M. Yeganeh,
Volume 40, Issue 2 (9-2021)
Abstract
In this study, microstructural changes in the thermomechanical processing and its effect on the corrosion behavior of 321 austenitic stainless steel were investigated. EDS analysis and optical microscopy were used to identify precipitates and microstructure, respectively. To evaluate the corrosion properties, potentiodynamic polarization test and electrochemical impedance spectroscopy were performed. First, the as-received sample was subjected to cold rolling with a 90% thickness reduction at liquid nitrogen temperature, and then annealing was performed at temperatures of 750, 850, and 1050 °C for 10 min. The results showed that severe cold rolling slightly improved the corrosion properties and in annealed samples, the corrosion resistance increased with more uniform microstructure, more reversion of martensite phase to austenite, and reduction of grain size. Annealed samples at 850 °C and 1050 °C with polarization resistance values of 8.200 kΩ.cm2 and 3.800 kΩ.cm2 depicted the highest and lowest corrosion resistance compared to other samples, respectively.
F. Fareghdeli, M. Karimi, A. Novin, M. Solati-Hashjin,
Volume 40, Issue 3 (11-2021)
Abstract
One challenge in preparing polymer/ceramic composites is non-uniform ceramic particles distribution in a polymer matrix. This research evaluated the effect of stirring time and temperature on hydroxyapatite (HA) distribution through (polylactic acid) PLA matrix. Therefore, to mix the ceramic suspension with the polymer solution, three temperatures, namely 25, 37, and 45°C and four times including 6, 12, 24 and, 48 h were examined. Fourier-transform infrared spectroscopy (FTIR) analysis was used to investigate the bonds, which showed physical bond formation such as carboxyl-calcium-carboxyl between HA and polymer matrix, influenced on particles distribution. Scanning electron microscopy (SEM) and Energy-dispersive X-ray spectroscopy (EDS) were used to observe particles distribution and determine samples homogeneity. To fulfill this goal, each obtained photograph representing the calcium presentation was split into nine equal sections, and a method based on the newly defined index called dispersion factor “α” was used to analyze the distribution. Results showed that the sample prepared at 37°C and 48 h had the topmost homogeneity properties.
P. Verdi, S. M. Monirvaghefi, F. Ashrafizadeh,
Volume 40, Issue 3 (11-2021)
Abstract
Regarding to the low rate of conventional Ni-P electroless plating method that needs more time to make a coating on the substrate surface, a new technique called “substrate local heating” was introduced based on the temperature parameter modification and its advantages were expressed and compared to the conventional electroless plating technique (temperature=90°C, pH=4.7). In order to provide necessary equipment making this approach practicable, electrical resistance was used as the heating source, and air injection and cooling water circulation were employed to control the solution temperature near the substrate and in the bulk solution, respectively. Considering the heater power (1000 W), the substrate and bulk temperatures were about 190°C and 80°C, respectively. This novel method could enhance the plating rate up to 32 µm/h which was about 60% greater than that of the conventional method, 20 µm/h. Moreover, benefits such as local plating, reduction of production costs, and formation of functionally graded coatings (FGC) can be achieved.
O. Ganji, S.a. Sajjadi, M. Mirjalili, Z.g. Yang,
Volume 40, Issue 4 (3-2022)
Abstract
Carbide coatings, due to their excellent anti-wear properties, are used to extend the life of molds exposed to abrasion forces. Various processes have been applied to produce carbide coatings. Thermo-reaction diffusion (TRD) using a molten salt bath could be considered as an economical method compared to other coating processes. In this study carbide-composite coatings using molten salt baths composed of oxides of carbide forming elements (chromium and vanadium) on SKD-11 and T10 tool steels at 1000 ℃ were formed. The results showed that the coatings included chromium carbide phases: CrC, Cr7C3, and Cr23C6 as well as vanadium carbide: VC, VC0.88, V6C5, V8C7, and a triple phase with the composition of Cr2C2V. The highest hardness (1890-2020 HV) and the lowest coefficient of friction (0.14) were achieved by the carbide coating of T10 steel with the second bath of vanadium oxide.
N. Ghobadi, S. A. Hosseini Moradi, M. Amirzade,
Volume 40, Issue 4 (3-2022)
Abstract
In this research, cobalt ferrite powders (CoFe2O4) and cobalt ferrite/reduced graphene oxide composite (CoFe2O4/RGO) were synthesized by the co-precipitation method. The phase structure, morphology, magnetic properties, and microwave absorption properties of the produced samples were investigated through various techniques. X-ray diffraction test indicated the successful formation of pure CoFe2O4 and its composites with RGO. According to the Scanning electron microscopy (SEM) images, most pure and composite samples’ particles were formed in a semi-spherical shape. The VNA test results showed the saturation magnetization of CoFe2O4 and the composite containing 5 wt.% and 10 wt.% of RGO, 71.6, 56, and 37 emu/g, respectively. Also, the network analyzer results demonstrated the maximum reflective losses in the X-band range due to the impact of microwaves on CoFe2O4 te was -5.5 db. This amount reached 21.5 dB with the addition of 10 wt.% RGO. Also, the wave input increased from 41% for the pure CoFe2O4 to 99.5% for the sample containing 10 wt.% RGO.
H. Fallah-Arani, N. Riahi-Noori, S. Baghshahi, A. Sedghi, F. Shahbaz Tehrani,
Volume 40, Issue 4 (3-2022)
Abstract
In this research, the effect of addition of silicon carbide (SiC) nanoparticles on the improvement of the structural, superconductivity, magnetic, and flux pinning properties of high-temperature superconductor Bi1.6Pb0.4Sr2Ca2Cu3O10+θ (Bi-2223) was investigated. The Bi-2223 ceramic superconductor was prepared using the sol-gel method, and silicon carbide nanoparticles were modified by Azobisisobutyronitrile (AIBN). The X-ray diffractometry, feild emission scanning electron microscopy, magnetic susceptibility, and hystersis loop measurements were performed to characterize the synthesized compounds. Based on the magnetic measurements, the superconductivity transition temperature dropped with an increase in the content of nanoparticles. Also, the maximum magnetization, hysteresis loop width, critical current density, and magnetic flux pinning force belonged to the sample with 0.4 wt.% SiC nanoparticles.
M. H. Rezvani, M. Yeganeh, S. M. Lari Baghal,
Volume 41, Issue 1 (8-2022)
Abstract
In this study, the addition of organic methionine inhibitor (as an eco-friendly inhibitor) to 0.1 M sulfuric acid media on corrosion resistance of 316L austenitic stainless steel (fabricated by rolling method and three-dimensional (3D) printing method) was investigated. Open-circuit potential electrochemical test and impedance, and structural tests such as optical and electron microscopy and x-ray photoelectron spectroscopy were conducted. The results showed that the corrosion resistance in the presence of inhibitor was higher than the sample without inhibitor and the inhibitory efficiency of methionine was increased up to 64% and the resistance to surface transfer between metal oxide and electrolyte was improved up to 2.77 times. The addition of methionine reduced the surface roughness and accumulation of the surface cavities. The chemical and physical adsorption mechanism of the inhibitor (negatively charged side adsorption of the methionine molecule with positively charged anodic regions of the metal surface) occurred at all points on the surface of the sample with the inhibitor. Also, the amount of oxygen in the cavities was reduced and the distribution of sulfur was uniform. The thickness of the passivator oxide layers was calculated more than the sample without inhibition due to the addition of inhibitor.