In this study, the effect of mechanical alloying on the microstructure and phase constituents of Mg-6Al-1Zn-1Si system was investigated. To understand the thermal behavior, isothermal annealing was performed at three different temperatures of 350, 400 and 450 °C for 1h. The results showed the grain size initially decreases with increasing the milling time up to 35h and then slightly increases. In contrast, the lattice strain increases sharply with increasing the milling time up to 35h and then decreases. Second-phase intermetallic particle Mg2Si was produced during annealing and the amount of this phase was increased with increasing annealing temperature. The mechanical alloying process decreased the formation temperature of Mg2Si.

---

In this study, the effect of Al₂O₃ addition as a diluent during mechanically activated self-propagating high temperature synthesis (MASHS) of Al₂O₃-ZrB₂ composite was investigated. For this purpose, the thermite mixture of Al, ZrO₂, H₃BO₃ and different amounts of Al₂O₃ (0, 3, 6, 9 wt.%) were used as the raw materials and mechanically activated for 5 h, then furnace sintering was performed at 650 °C. The results showed that by increasing the Al₂O₃ content up to 6 wt.%, the intensity of exothermic peak in the DSC curves increases, but for higher additive contents it decreases. In this case, more homogenous distribution of ZrB₂ particles with finer grain size was observed.