A. Azimi Dastgerdi, F. Ashrafizadeh, M. R. Toroghinejad, F. Shahriari , H. Zahraei,
Volume 30, Issue 2 (12-2011)
Abstract
In this paper, bare spot defects in hot-dip galvanized sheets were studied in terms of the microstructure and their influence on the corrosion and mechanical properties. Surface characteristics and microstructural features were examined by scanning electron microscopy equipped with energy dispersive spectroscopy microanalysis system. The results showed that the major cause of the bare spots was the lack of wetability of the sheet surface due to contamination, improper heat treatment or chemical composition. Corrosion resistance was evaluated by standard salt spray test. Mechanical properties were examined by tensile testing. The time to red rust was much shorter on the bare spots as compared to other regions, but it appeared that bare spot defects had no significant effect on the mechanical properties of the galvanized steel sheets.
B. Bakhit, A. Akbari,
Volume 31, Issue 2 (12-2012)
Abstract
Composite and nanocomposite Ni-Co/SiC coatings were synthesized by electro-codeposition of micro and nano-sized SiC particles with average diameter of 10m and 20nm using horizontal electrodes. Surface morphology, chemical composition, phase composition, hardness and corrosion resistance of the deposited coatings were studied using SEM observations and EDX, XRD, microhardness and polarization measurements as a function of the electrodeposition current density. The results indicated that the nanocomposite coatings exhibit higher hardness and corrosion resistance compared with the composite coatings containing micro-sized SiC particles despite their lower percentage of the SiC content. The maximum hardness values of 615HV and 490HV were obtained for nanocomposite and composite coatings deposited at current density of 3A/dm2. The observed properties were discussed based on the structural details.
M. Alizadeh, A. Cheshmpish,
Volume 37, Issue 2 (9-2018)
Abstract
In this research, Ni-Mo-Al2O3 composite coatings were electro-deposited on the mild carbon steel in a citrate bath containing micro- sized Al2O3 particles. Afterward, the effect of the particle concentration in the electrolyte bath (ranging from 0 g/L to 30 g/L) on the microstructure, microhardness, and corrosion performance was evaluated. To investigate the microstructural changes and the surface morphology of the coatings, as well as the particle distribution in the deposits, optical and scanning electron microscopy coupled with the energy dispersive X-ray spectroscopy was utilized. The corrosion behavior of the prepared coatings was investigated in a 3.5 wt. % NaCl solution. The results showed that the presence of the Al2O3 particles in the Ni-Mo coatings changed the microstructure and also, increased the microhardness and corrosion resistance of them. It was also found that the desirable structure of the protruding crystallite morphology with no detectable pores could be achieved at the medium concentrations of reinforcement (e.g. 20 g/L). Further the optimum concentration of the particles in the electrolyte bath to attain the composite coating with the desirable microstructure and consequently, the desirable corrosion resistance was found to be 20 g/L.