M. H. Enayati and M. Salehi,
Volume 25, Issue 2 (1-2007)
Abstract
Fabrication and characterization of aluminum matrix composites containing different volume fractions of Ni3Al powder (5-40 Vol%) were investigated. Ni3Al powder was produced by mechanical alloying of elemental nickel and aluminum powder mixture. Al-Ni3Al composite parts were prepared using a powder metallurgy route involving two stages Al and Ni3Al powder mixtures were first compacted under 500MPa and then hot-pressed under 250MPa at 420 oC for 10min. The microstructure and hardness of consolidated parts were investigated by x-ray diffractometery, optical and scanning electron microscopy and
hardness measurements. Results showed that consolidated Al-Ni3Al samples included no significant porosity with a nearly uniform distribution of Ni3Al particles. Additionally, structural examinations showed that no significant reaction between Ni3Al and aluminum matrix occurred during sintering process. Al-Ni3Al composites exhibited a higher hardness value compared with pure aluminum sample prepared under identical conditions. The hardness value of Al-Ni3Al composites increased linearly as Ni3Al content increased.
S. Shahzamani, M. R. Toroghinejad, A. Asharfi,
Volume 40, Issue 2 (9-2021)
Abstract
In this study, Al/Al2O3 composite was produced by accumulative roll bonding (ARB) process coupled with the plasma electrolytic oxidation (PEO) process. The alumina was grown on Al sheets by electrolyte technique with three different thicknesses (10, 20, and 40 µm). The results showed that incorporation of alumina up to 3.22 vol.% in aluminum matrix enhanced the yield and tensile strength of the composite, whereas increasing the amount of alumina up to 6.25 vol.% deteriorated the tensile properties. In the last part, a serial sectioning process was employed to develop a three-dimensional (3D) representation of the microstructure of Al2O3 particles reinforced Al composite for visualization and finite-element modeling (FEM).