M. Mashhadi, A. Abdollahi, Z. Nasiri,
Volume 33, Issue 2 (3-2015)
Abstract

In this study, ZrB2-HfB2 composite was produced by pressureless sintering method. MoSi2 B4C and SiC particles were used as reinforcement. ZrB2 powder was milled in planetary ball mill apparatus and then reinforcement particles were added to the milled powder. The composite powders were then CIPed and sintered at 2100oC and 2150oC. Scanning electron microscopy (SEM) with an energy dispersive X-ray spectrometer (EDS), flexural test, and resonance frequency method were used to compare the added particle effects on mechanical properties and pressureless sintering behavior of ZrB2-HfB2 composite. The analysis showed that the ZrB2-HfB2-MoSi2-SiCnano composite displays the largest gain in flexural strength. Furthermore, increasing the sintering temperature leads to an increase in flexural strength of samples.
M. Shirvani, M. Mashhadi, M. Yosofi,
Volume 38, Issue 4 (1-2020)
Abstract

In this research, solid state carbothermal synthesis of HfB2 Nano powders was investigated. For this purpose, HfO2,H3BO3, carbon active or phenolic resin were used as raw materials for carbothermal reaction. After 2-4 hours of milling the raw materials by a planetary ball in an ethanol media, the mixture was heat dried and pressed in to disks under pressure of 20-30 bar. The disks were then placed in a graphite crucible and heat-treated at 1500–1600 °C for 1 hour under flowing Ar atmosphere. The powder product was analyzed by X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and backscattered electron (BSE) imaging. The heat treatment temperature, amount of boric acid, milling and heat treatment time were recognized as four factors influencing synthesis and size of HfB2 powder particles. SEM images reported irregular morphologies with a particle size of about 2-4 µm for HfB2 powder. The best sample was obtained at a molar ratio of HfO2 : phenolic resin carbon: boric acid = 1:5:5 at 1600 °C after 1 hour of heat treatment. XRD results confirmed synthesis of pure HfB2 with a crystallite size of about 60 nm.


Page 1 from 1     

© 2025 CC BY-NC 4.0 | Journal of Advanced Materials in Engineering (Esteghlal)

Designed & Developed by : Yektaweb