The Comparison of Microstructure and Mechanical Properties of Diffusion Joints of 5754, 6061, and 7039 Aluminum Alloys to AZ31 Magnesium Alloy
M. Jafarian, M. Paidar, M. Jafarian,
Volume 35, Issue 1 (6-2016)
Abstract

In this study, microstructure and mechanical properties of diffusion joints between 5754, 6061 and 7039 aluminum alloys and AZ31 magnesium alloy were investigated. Diffusion joints were done between the alloys at 440 °C, for duration of 60minutes, at 29 MPa pressure and under 1×10-4 torr vacuum. The interface of joints was studied using optical (OM) and scanning electron microscopy (SEM) equipped with EDS analysis and the line scan. According to the results of EDS analysis, the presence of intermetallic compounds including Al12Mg17, Al3Mg2 and their mixture was observed at the diffusion zone. Also, according to the results of the line scan, the hardness value of aluminum alloys has a considerable effect on diffusion of the magnesium atoms toward aluminum alloy and the greatest diffusion of magnesium was observed when 6061 aluminum alloy was used. More diffusion resulted in a stronger bond between atoms of magnesium and aluminum, and maximum strength of approximately 42 MPa was obtained when 6061 aluminum alloy was used.


Investigating the Effect of Equal Channel Angular Extrusion on Microstructure and Mechanical Properties of the 60-40 Two-phase Brass Alloy
S. E. Mousavi, M. Meratian, A. Rezaeian,
Volume 36, Issue 4 (3-2018)
Abstract
Equal Channel Angular Pressing (ECAP) is currently one of the most popular methods for fabricating Ultra-Fine Grained (UFG) materials. In this study, mechanical properties of the 60-40 two phase brass processed were evaluated by ECAP. The samples were repeatedly ECAP-ed to strains as high as 2 at a temperature of 350 ◦C using route C. The microstructure of the samples showed that small grains were formed in the boundaries which indicates the occurrence of recrystallization in different passes. Observation of slip trace in the microstructure of the samples showed that even in such alloy with a low-stacking fault energy, dislocations slip trigger the deformation. Investigation of mechanical properties showed that with increasing the number of passes, tensile strength, microhardness and ducility improved at the same time.
 

TIG Surface Alloying of Ti-6Al-4V with Nitrogen and Chromium for Improved Tribological Properties
G. R. Faghani, A. R. Khajeh-Amiri,
Volume 38, Issue 4 (1-2020)
Abstract
Due to special properties such as low density, high strength and high corrosion resistance Ti-6Al-4V alloy has been used extensively in various industries, especially in the aerospace aspects. However the major problem of this alloy is its poor tribological properties under relatively high loads. In the present study, in order to improve the tribological properties of mentioned alloy, chromium particles were added to Ti-6Al-4V layers in the nitrogen-containing atmosphere during the Tungsten Inert Gas (TIG) welding process. Microstructural investigations using optical microscopy, X-ray diffraction analysis and scanning electron microscopy, proved the formation of TiN, TiCr2 and Cr2N particles in the matrix of hard titanium phase. The hardness of TIG alloyed layer increased to 1000 HV0.3 which was 4 times higher than that of the base alloy. Moreover, the wear rate of TIG alloyed samples with chromium and nitrogen under 30N load and distance of 1000 m was 5.9 times lower than that of the bare Ti-6Al-4V alloy.

INVESTIGATING THE EFFECT OF WELDING PASTE CONTAINING GRAPHENE NANOSHEETS ON BONDING PROPERTIES OF WELDED AISI 304 STAINLESS STEEL PRODUCED BY FLUX-CORED ARC WELDING
M. Khosravi , M. Mansouri, A. Gholami, Y. Yaghoubinezhad,
Volume 40, Issue 1 (5-2021)
Abstract
In this research, the effect of graphene oxide (GO) and reduced graphene oxide (RGO) nanosheets on the mechanical and microstructural properties of AISI 304 stainless steel welded joints produced by the flux-cored arc welding (FCAW) method was investigated. Light microscope, field emission scanning electron microscope (FE-SEM) equipped with energy-dispersive X-ray spectroscopy (EDS), X-ray diffraction analysis (XRD), Raman spectroscopy, and tensile strength test were used to characterize the samples. GO was synthesized by modified Hummers’ method and reduced by hydrazine. Accordingly, the pastes of GO and RGO in different concentrations of 1, 3, and 10 mg/ml were applied in the groove. The results demonstrated that increasing the RGO concentration up to 10 mg/ml improves the tensile strength and hardness values of welded joints up to 23% and 43%, respectively. It seems that RGO nanosheets have a significant effect on the mechanical properties of the welded joints by pinning of dislocations.