Showing 11 results for Welding
M. Shamanian, A. Saatchi, M. Salehi and T. H North,
Volume 21, Issue 2 (1-2003)
Abstract
The metallurgical and mechanical properties of Ti6Al4V/(WC-Co) friction welds have ben investigated. The microstructure close to the bondline comprised a mixture of acicular and equiaxed α plus β phases. The diffusion of elements in the welded specimens has been detected. The fracture strengths of Ti6Al4V/(WC-Co) friction welds markedly improved when the cobalt content in the (WC-Co) carbide substrate increased.
During the three-point bend testing of Ti6Al4V/WC-6wt.%Co welds, the crack initiated at the bondline region at the periphery of the weld and then propagated into the brittle (WC-6wt.%Co) substrate, while with the Ti6Al4V/WC-11 wt.%Co and Ti6Al4V/WC-24wt.%Co welds, the crack initiated and propagated at the bondline region.
Keywords: Friction welding, Ti6Al4V alloy, Cemented tungsten carbide, Microstructure, Fracture strength
A.h. Khosrovaninezhad, M. Shamanian, A. Rezaeian , M. Atapour,
Volume 34, Issue 2 (7-2015)
Abstract
This paper reports on the mechanical properties of the dissimilar joints between AISI 316 austenitic stainless steel and St 37 low carbon steel achieved using friction stir welding technique. The welding was carried out by means of rotational speed of 800 rpm and linear speeds of 50,100,150 mm/min. EDS and XRD techniques were employed in order to determine possible phase transformations. Tensile test, shear punch test and microhardness measurements were conducted to evaluate the mechanical properties of the joints. The results of phase investigations showed that no carbide and brittle phase were detected at the joint boundary. Also, tensile test results demonstrated that failure occurred in the St 37 base metal. According to the shear punch test, the highest ultimate shear strength and yield shear strength was achieved for the sample welded at rotational speed of 800 rpm and linear speed of 150 mm/min, while this sample showed the least elongation. In addition, the highest microhardness was measured in the stir zone of austenitic stainless steel sample welded in the above mentioned welding condition, which can be attributed to the decrease in grain size caused by recrystallization process.
F. Bodaghi, M. Atapour, M. Shamanian,
Volume 34, Issue 3 (12-2015)
Abstract
Aluminium 5xxx alloys excellent properties make them suitable for many industrial applications. The corrosion behavior of this alloy family in industrial environments such as sea water is the main focus of many researches. Due to need for joining large segments of this alloys, the effect of single as well as multipass (double and triple pass) gas metal arc welding (GMAW) on microstructure and corrosion behavior of Al5083-H321 alloy was studied. For this purpose, ER5183 filler metal was used. Microstructures were evaluated using optical and scanning electron microscopy (SEM). Corrosion measurements were performed using open circuit potential test, immersion test in 3.5%NaCl solution and polarization tests. Results indicated that the corrosion resistance of the two passes weldment was improved in comparison with the base metal and its icorr and Ecorr were equal to 0.087´10-6 (µA/cm2) and -0.4395 (V), respectively.
Seyed M. Ahl Sarmadi, M. Shamanian, H. Edris, M. Atapoor, A. Behjat, M. Mohtadi Bonab, J. Szpunar,
Volume 36, Issue 1 (6-2017)
Abstract
Super duplex stainless steel is a kind of duplex stainless steel that has pitting resistant equivalent number over than 40. Unified Numbering System (UNS) S32750 is a common super duplex stainless stee, that is mostly applied in oil and gas refinery industries, because of its proper corrosion-resistant properties . Therefore, joining of these steels by welding is very important, but the greatest problem in this regard is the corrosion and decrease in mechanical properties after welding.. In this research, UNS S32750has been joined by friction stir welding method. The tool being used in this research was a WC with 16mm shoulder diameter, 5 mm pin diameter, and 1.9 mm height. X-ray diffraction showed that harmful phases, such as sigma or chi have not been formed. Microstructure study indicated that grain size in the stir zone has decreased. Vickers Hardness Test Method has been applied on welded samples. Moderate microhardness of base metal was 285 Vickers but, the microhardness increased in the stir zone to 360 Vickers, because of decreasing the grain size. The cyclic polarization determined that potential and corrosion current of joint metal by friction stir welding method was similar to base metal. Also, it was revealed that ferrite percentage in the stir zone doesn't decrease very much because the friction stir welding heat input is very low and the colding rate is very high.
M. Poorkabirian, H. Mostaan, M. Rafiei,
Volume 36, Issue 2 (9-2017)
Abstract
In this research, dissimilar welding between 4130 low alloy steel and austenitic stainless steel 316L has been investigated using Gas Tungsten Arc Welding (GTAW). Two types of filler metals, including ERNiCr-3 and ER309L, were used for this purpose. Moreover, the joint microstructures including the weld metals, heat affected zones and interfaces were characterized by optical and Scanning Electron Microscopy (SEM). The mechanical behavior of the joint was tested by impact and tension tests. Observations by SEM showed that in impact test, the fracture is soft. In the tensile test, the welded sample by ER309L filler metal was fractured from 316L base metal, but welded specimen with ERNiCr-3 was fractured from welded zone. Also, the results showed a dendritic structure in the nickel-based weld metal. No crack was found in the cellular-dendritic microstructure of ER309L weld metal due to the existance of delta ferrite between them.
M.r. Khanzadeh Gharah Shiran, H. Bakhtiari, M. Mohammad Javadi,
Volume 36, Issue 3 (11-2017)
Abstract
In this research, the effect of standoff distance and explosive material thickness on metallurgical features of explosive welding connection of copper to 304 stainless steel has been investigated. Experimental analysis were performed using optical microscopy, scanning electron microscopy, microhardness test and tensile shear strength test. The results indicated that due to severe plastic deformation in welding, both grain elongation and refinement occurred near the connection. Also, increasing of welding parameters led to an increase in the locally melted zones. The results showed that chemical composition of the melted zone consisted of elements of both flyer and base plates. By decreasing the explosive material thickness and standoff distance, the hardness of copper interface zone decreased from 103.4 HV to 99.8 HV. Moreover, increasing the temperature in stainless steel connection led to decreased hardness. As such, the maximum tensile shear strength of 244 MPa was observed in the sample with 79 mm explosive thickness and 3 mm standoff and the minimum tensile shear strength of about 208 MPa in the sample with 46 mm explosive thickness and 3 mm standoff. By decreasing explosive thickness and standoff, the bond strength decreased, too.
M. R. Pakmanesh, M. Shamanian, S. Asghari,
Volume 36, Issue 4 (3-2018)
Abstract
In the present study, the optimization of pulsed Nd:YAG laser welding parameters was done on a lap-joint of a 316L stainless steel foil in order to predict the weld geometry through response surface methodology. For this purpose, the effects of laser power, pulse duration, and frequency were investigated. By presenting a second-order polynomial, the above-mentioned statistical method was managed to be well employed to evaluate the effect of welding parameters on weld width. The results showed that the weld width at the upper, middle and lower surfaces of weld cross section increases by increasing pulse durationand laser power; however, the effects of these parameters on the mentioned levels are different. The effect of pulse duration in the models of weld upper, middle and lower widths was calculated as 76, 73 and 68%, respectively. Moreover, the effect of power on theses widths was determined as 18, 24 and 28%, respectively. Finally, by superimposing these models, optimum conditions were obtained to attain a full penetration weld and the weld with no defects.
S. Asghari, A. M. Eslami, A. Taheri Zadeh, N. Saeidi,
Volume 39, Issue 3 (12-2020)
Abstract
In this study, the effect of welding heat input on microstructure and mechanical properties of dissimilar joints of API-X42 and API-B pipeline steels was investigated. Evaluation of the microstructures showed that increasing the welding heat input decreased acicular ferrite in weld metal microstructure, while amount of Widmanstatten ferrite, polygonal ferrite and grain boundary ferrite increased. Also, results of microhardness test showed that by increasing the heat input, hardness of weld metal and the heat affected zone decreased. Tensile test results showed that as the heat input increased, fracture transferred from base metal of API-B to the heat affected zone. Impact test results also showed that increasing the welding heat input could sharply drop the impact energy of the heat affected zone for both base metals due to extensive grain growth.
R. Moradi, M. Roshanaee, H. Mostaan, F. Nematzadeh, M. Safari,
Volume 40, Issue 1 (5-2021)
Abstract
In this research, microstructure and mechanical properties of laser welded joints between 2304 duplex stainless steel and Inconel 718 nickel-based super alloy were investigated. Microstructural evolution in the various areas of welded joints and also the effect of welding parameters on the mechanical properties of dissimilar joints were studied. Response surface methodology based on the central composite design was used in order to find the optimum welding parameters. Effective parameters of the welding process including laser power, travel speed and defocusing distance were set in the range of 1000 to 1900 W, 1 to 5 mm/s and -1 to 1 mm, respectively. Uniaxial tensile test was used to evaluate the fracture force of weld joints. The microstructural observations and phase evolutions were studied using optical microscope. It was found that the fracture force of the weld joints firstly increased by travel speed and defocusing distance and then decreased by further increase. The maximum fracture force was obtained when laser power, travel speed and defocusing distance were 1900 W, 3 mm/s and 0 mm, respectively. The center line of weld metal was mainly consisted of equiaxed grains where, columnar grains were formed in the fusion line. The obtained results from the hardness measurement showed that the hardness of Inconel 718 was decreased due to dissolution of TiC and NbC particles.
M. Khosravi , M. Mansouri, A. Gholami, Y. Yaghoubinezhad,
Volume 40, Issue 1 (5-2021)
Abstract
In this research, the effect of graphene oxide (GO) and reduced graphene oxide (RGO) nanosheets on the mechanical and microstructural properties of AISI 304 stainless steel welded joints produced by the flux-cored arc welding (FCAW) method was investigated. Light microscope, field emission scanning electron microscope (FE-SEM) equipped with energy-dispersive X-ray spectroscopy (EDS), X-ray diffraction analysis (XRD), Raman spectroscopy, and tensile strength test were used to characterize the samples. GO was synthesized by modified Hummers’ method and reduced by hydrazine. Accordingly, the pastes of GO and RGO in different concentrations of 1, 3, and 10 mg/ml were applied in the groove. The results demonstrated that increasing the RGO concentration up to 10 mg/ml improves the tensile strength and hardness values of welded joints up to 23% and 43%, respectively. It seems that RGO nanosheets have a significant effect on the mechanical properties of the welded joints by pinning of dislocations.
F. Harati, S. M. Mousavizadeh, M. A. Jabbareh,
Volume 41, Issue 1 (8-2022)
Abstract
Cast AZ91 alloy is one of the most used magnesium alloys, which is sensitive to liquation in the fusion weld method,s and friction stir spot welding due to low eutectic temperature and the presence of the intermetallic compound in eutectic temperature. In this research, the liquation behavior of AZ91 alloy during friction stir spot welding was investigated. The process was carried out at two rotation speeds of 1000 and 2500 rpm and a dwell time of 1 second on the plate of AZ91 with a 10 mm thickness. Microstructural characterization was carried out using optical and scanning electron microscopes. The results showed that at low rotation speed (1000 rpm), mechanical grinding redistribution and dissolution of 𝛾-Mg17Al12 precipitates occurred. While at high rotation speed (2500 rpm), the predominant phenomenon was liquation. In this condition, the liquation initiated around the 𝛾 phase, and then the liquid re-solidified, leading to the typical eutectic structure instead of initial 𝛾 precipitates. Moreover, the liquation intensified by approaching the stirred zone. Also, the presence of liquid film along grain boundaries resulted in decreased grain boundary strength and liquation cracking.