A. Lori Amini, H. Sabet, M. Ghanbari Haghighi ,
Volume 6, Issue 2 (Journal OF Welding Science and Technology 2020)
Abstract
In this investigation, the AISI 2205 duplex stainless steel was welded in the form of bead on plate by A-TIG process with different amount of the ZrO2 and TiO2 activated fluxes. The results of the visual inspection showed that the specimen with 50% ZrO2 and 50% TiO2 activated flux, had the lowest face width and the specimen with contains 90% ZrO2 activated flux, had the highest penetration depth. Also, the results showed that the angular distortion of the specimens with mix of the ZrO2 and TiO2 activated flux were 225% less than the specimen without activated flux. The results of macroscopic examination of different samples showed that the maximum length and width of the macroscopic grains were related to the sample with 90% ZrO2 activated flux and the smallest length and width of the macroscopic grains were related to the sample with 90% TiO2 activated flux. The hardness test results showed that the highest hardness of the samples was gained to 90% TiO2 activated flux specimen with 950 HV and the lowest hardness value for the sample with 90% ZrO2 activated flux with 410 HV. The results of all tests showed that surface activated fluxes (ZrO2 and TiO2) affected to the depth of penetration, face width, angular distortion, length and width of macroscopic grains and the hardness of weld metal by changing the longitudinal and transverse melt flow in the weld pool.
P. Chamani, H. Sabet, M. Ghanbari Haghighi,
Volume 9, Issue 2 (Journal OF Welding Science and Technology 2024)
Abstract
In this study the effect of rotational speed and tool angle parameters on the microstructure and mechanical properties of the AZ91/CP-Ti joint was investigated, for this reason the sheets with 4 x 26 x 100 mm dimensions were prepared and joint by FSW with different rotational speed (800, 1200 and 2500 rpm) and the tool angle (0.5, 1 and 3 degrees). After joining, the samples were cut and prepared for study of microstructural and mechanical properties. OM and SEM examination shows that the structure of AZ91/CP-Ti nugget zone includes alpha grains and the microstructure of the mix zone on the AZ91 side includes α-magnesium coaxial grains with Mg17Al12 intermetallic compounds. The results of the tensile test show that the maximum tensile strength value (160 MPa) related to the rotation speed of 2500 rpm and the tool angle of 1 degree. It was also determined that the rotation speed of 800 rpm was not suitable for joining of AZ91/CP-Ti. On the other hand, it was observed that by increasing the tool angle the work piece, initially leads to an increases the strength from 141 MPa to 160 MPa and then decreases to 132 MPa. the results of the Vickers hardness test show that the average of the nugget zone hardness was to 173, which is higher than the hardness of AZ91 alloy (61 Vickers) and near to the hardness of CP-Ti (167 Vickers).