M. H. Fathi, Gh. Feizi, Sb. Moosavi, Gh. Gahanshahi, M. Salehi, A. Saatchi and V. Mortazavi,
Volume 20, Issue 1 (7-2001)
Abstract
Hydroxyapatite coatings have been used on metallic substrates in a variety of applications, including modifying the surface of human implants, bone osseointegration and biological fixation. In this paper, the effects of various kinds of metallic substrate on clinical and pathological results of in vivo tests are presented. Four kinds of endodontic implants i.e, stainless steel, cobalt base alloy, plasma sprayed hydroxyapatite coated stainless steel, plasma sprayed hydroxyapatite coated cobalt base alloy were prapared and implanted in mandibular canine of
cats. After a healing period of 4 months, investigation by SEM and histopathological interpretation and evaluation showed significant differences in tissue response and osseointegration between coated and non-coated metallic implants. It was concluded that the results were affected by the kind of metallic substrate .
Keywords: Hydroxyapatite coating, Dental endodontic implant, Osseointegration, Corrosion, Stainless steel,
Cobalt base alloy
K. Raeissi, A. Saatchi and M. A. Golozar,
Volume 23, Issue 2 (1-2005)
Abstract
On electropolished steel at low current densities, morphology and texture of electrodeposited zinc were investigated. Zinc coating is consisted of hexagonal crystallites laid on each other to produce packets. These packets are of different sizes and are stacked in different orientations to construct a homogeneous coating on steel substrate. This coating does not have texture, i.e., it has a random texture. With increasing current density, the morphology changes completely as each grain attains a special orientation. In this case, coating has a strong basal plane (0002) along with low angle planes (1013 and 1014). Coating obtained on mechanically polished surfaces consists of individual packets of zinc crystals, which are near each other with different
orientations. These coatings have a higher density of basal plane (0002) in comparison to electropolished surfaces. The morphology and texture variations with cathodic polarization and surface preparation of steel are due to their effect on nucleation and growth.
K. Zangeneh Madar and S. M. Monir Vaghefi,
Volume 23, Issue 2 (1-2005)
Abstract
In the present stady, thermochemical treatment in H2/NH3 atmosphere was used as a post-treatment for electroless Ni-P coatings on the AISI 4140 steel substrates. High phosphorus (9%) coatings with thicknesses of 2, 24 and 48 m were applied and the effects of the thermochemical treatment on the morphology, structural changes, roughness, hardness
and wear resistance of coatings were studied by SEM, EDS, XRD, profilometry, and microhardness tester. Wear test was used to evaluate wear characteristics of coatings. The wear behaviour of the thermochemical treated/Ni-P coated samples was assessed by comparison with thermochemical treated/uncoated (nitrided) samples. The results showed that effect of thermochemical treatment varies with the coating thickness. In addition, it was shown that a multicomponent coating containing phosphide, nitride and intermetallic phases as well as diffusion region can be developed in the thin (2 m) electroless Ni-P coated steel by thermochemical treatment. This sample showed better wear resistance than 24 m Ni-P coated steel under higher load. This behavior was ascribedto nitride phases formed at the surface as well as a nitrogen diffusion zone at the subsurface of thin Ni-P coated steel
A. Nasr-Esfahany and M.heydarzadeh Sohi,
Volume 23, Issue 2 (1-2005)
Abstract
Zinc-Nickel electrodeposits have been widely adopted for surface treatment of automobile steel sheet for high corrosion resistance. In this work the effect of pulse parameters on the Zn-Ni alloy electrodeposits was investigated. The hardness, thickness, corrosion resistance and composition of deposits thus produced were investigated. The surface topography of the deposits was also observed in SEM and results are reported. It has been shown that the thickness of the pulse electrodeposits
was almost even. The hardness in the pulse electrodeposits increased by increasing the on-time period and by decreasing the current density. It was also noticed that increasing the on-time period increases the nickel content of the deposit. Pulse electrodposits had fine structure and the structure become finer by reducung the on-time period and pulse frequency. The corrosion dehaviors of the deposits were then investigated. The results showed that the corrosion resistance of the DC electrodeposits improves in their nickel content increases. Pulse electodeposits show the same behavior, but deposits with about 13% nickel show maximum corrosion resistance.