Safarbali B, Shamanian M, Eslami A. Effect of Post-weld Heat Treatment on Joint Properties of Dissimilar Friction Stir Welded AA2024 and AA7075 Aluminum Alloys . JWSTI 2019; 5 (1) :1-11
URL: http://jwsti.iut.ac.ir/article-1-252-en.html
Effect of Post-weld Heat Treatment on Joint Properties of Dissimilar Friction Stir Welded AA2024 and AA7075 Aluminum Alloys
B. Safarbali1 , M. Shamanian * 1, A. Eslami1
1- Department of Materials Engineering, Isfahan University of Technology, Isfahan, Iran
Abstract:   (9717 Views)
In present study, the effect of heat treatment after friction stir welding dissimilar welds T6-7075 and T4-2024 aluminum alloys were investigated. Friction stir welding was performed at a constant rotation speed of 1140 rpm and welding speed 32 mm/min. After welding samples are taken under various heat treatment processes at different aging temperature and time period. Microstructural observations, phase analysis characterization and mechanical properties were performed on welded before and after heat treatment in cross section of welds joint. The results showed that post-weld heat treatment causes abnormal grain growth turns destructive effect on the mechanical properties, while formation of fine and uniform precipitation recovery strength and ductility of welds joints. It is found heat treatment based on T6-7075 and T6-2024 procedure has highest and lowest impact on the restore of weld strength. Tensile test indicate that fracture occurred on the interface between TMAZ and HAZ in retreating side (7075) at as-weld joint, if that failure happens in the stir zone by applying PWHT. Surface fracture suggested fractures in PWHT samples are predominantly inter-granular, while in as-weld joint the fractures of joints are mostly trans-granular.
Keywords: Friction Stir Welding, Heat treatments, Microstructure, Mechanical properties
Full-Text [PDF 2514 kb]   (2077 Downloads)    
Type of Study: Research | Subject: Special
Add your comments about this article : Your username or Email:
CAPTCHA
Rights and permissions
Creative Commons License This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.

© 2024 CC BY-NC 4.0 | Journal of Welding Science and Technology of Iran

Designed & Developed by : Yektaweb