Showing 3 results for Edris
M. Ahl Sarmadi, M. Shamanian, H. Edris, A. Behjat, M.a. Mohtadi Bonab, J. Szpunar,
Volume 1, Issue 1 (Journal OF Welding Science and Technology of Iran 2016)
Abstract
In this study the microstructure and mechanical properties of super duplex stainless steel UNS S32750 welding was studied. For this purpose, the method of gas tungsten arc and filler metal AWS ER2594 with a diameter of 4.2 mm was used. In order to investigate the microstructure light microscopy and electron microscopy equipped with backscatter electron diffraction were used. Mechanical properties were studied by hardness and tensile tests. Weld metal had Cast structure with austenite in the dendrite form located in ferrite matrix. It was also observed in the melting zone after welding, the ferrite volume fraction decreased to 50 percent 60% base metal ferrite) ,Due to the low cooling rates and high heat input method in the gas tungsten arc welding. Vickers micro-hardness test method was carried out on the samples showed that average about 285 Vickers hardness of base metal; however, hardness in the fusion region due to increased austenite fraction fell to 250 Vickers. But hardness in the heat-affected zone due to lower volume fraction of austenite and ferrite phase formation of chromium carbide intermetalic compounds increased to 340 Vickers. The results of the tensile test showed that the tensile strength decreased with increasing heat input, because of increase the size of grains due to the increased heat input.
M. Ahl Sarmadi, M. Shamanian, M. Atapour, H. Edris, A. Behjat,
Volume 3, Issue 1 (Journal OF Welding Science and Technology of Iran 2017)
Abstract
In this study, the corrosion behavior of super duplex stainless steel UNS S32750 and tungsten arc welding with filler metals AWS ER2594 duplex stainless steel in acidic solution containing chloride ions have been investigated. Microstructure of weld joints evaluateby light and electron microscope and corrosion behavior examine by open circuit potential and cyclic polarization tests.The results showed that increas in heat input leads to a change in the distribution of alloying elements, formation of intermetallic phases around grain boundaries and the shifting balance between austenite and ferritein phases in weld region. Based on the cyclic polarization tests, cross-weld and base metal active behavior and have good corrosion resistance due to the presence of high alloying elements. As well as increase in heat input leads to an increase in current density and decrease in the pitting potential.
, M. Ahl Sarmadi, M. Atapour, A. Behjat, H. Edriss, M. Vahman ,
Volume 4, Issue 1 (Journal OF Welding Science and Technology of Iran 2018)
Abstract
Galvanic corrosion is an ever-present problem in all different environments, particularly in tanks. The goal of this project is to develop a finite element model that can be used with experimental data to characterize the corrosion of a galvanic weldments couple in an electrolyte. In this study sample are welded by gas tungsten arc welding and friction stir welding. According to ASTM G8, Evaluation of corrosion properties examined with cyclic polarization test in 0.5 molar H2SO4 andthe information required to validate the model was prepared. The finite element model is developed using COMSOL and Math Module through derivation of equations describing corrosion thermodynamics and electrochemical kinetics. The results showed that reducing in heat input to improve galvanic corrosion behavior in the weld sample.In addition to result of simulation reveal sample that welded by gas tungsten arc method had higher current density galvanic corrosion in comparison with friction stir sample.