M. M. Taghvaei, H. Mostaan, A. Sonboli, H. R. Mansouri Gavari,
Volume 8, Issue 1 (Journal OF Welding Science and Technology 2022)
Abstract

In this study, DIN 34CrAlNi7 Nitriding steel in two states before and after nitriding, were welded by tungsten-gas arc welding process using two types of fillers (ER309L and ER312). The aim of this research was to investigate the best conditions for welding (before or after nitriding) and also to choose the best filler metal. The microstructure of the joint was examined using an optical microscope. A tensile strength test was also used to evaluate the mechanical properties. Fracture surfaces were also studied using a scanning electron microscope (SEM). According to the results Welding of these steels with ER309L filler is allowed only in the pre-nitriding state. If the base metal is nitriding, due to microstructural changes in the weld metal, filler metal ER309L cannot be used. However, the results of samples welded with ER312 filler metal show that if the base metal mixing percentage is less than 30%, this filler can be used for welding base metals in both before and after nitriding.

M. M. Taghvaei, M. Shamanian, Behzad Niroumand, H. Mostaan,
Volume 8, Issue 2 (Journal OF Welding Science and Technology 2023)
Abstract

Joining of Hastelloy C276 nickel-base superalloy to AISI316 Stainless Steel using BNi-2 interlayer performed by transient liquid phase process (TLP) at 1150°C for 5 and 30 minutes. Bonding microstructure was studied using an Optical microscope and a scanning electron microscope (SEM). Vickers hardness test and shear strength test have been used to evaluate the mechanical properties. Microstructural studies showed that at 5 and 30 minutes of bonding time, isothermal solidification is completely formed, and the Center of the joint is free of any eutectic intermetallic compounds. Also, Findings showed that the DAZ of Hastelloy C276 nickel-base superalloy contains rich borides of Ni, Cr, Mo, and W, and the DAZ of 316 austenitic stainless steel contains borides rich in Fe, Cr, and Ni.



Page 1 from 1     

© 2024 CC BY-NC 4.0 | Journal of Welding Science and Technology of Iran

Designed & Developed by : Yektaweb