Journal of Welding Science

316 steel is used in transportation, space, and chemical equipment. This steel is in demand in these industries due to its durability. It is used to increase the lifespan and renovate equipment. The research explores the impact of laser energy density on st6 cladding. It specifically focuses on the microstructure and geometric characteristics of the cladding. The cladding is applied on 316 steel. The experiment was designed with energy density changes from 40 to 116 J/mm and powder rate changes between 12 and 20 g/min. Optical and electron microscopic images were used to evaluate the samples. The results indicated that the dendritic arms grew larger with increased energy density. The dimensions increased from 1.5 to approximately 3. In other words, the speed of cooling is doubled. Increasing energy density from 40 to 75 J/mm reduced cobalt to chromium ratio from 2 to 0.7. It also decreased cobalt to iron ratio from 35 to 3. The changes emphasize how energy density affects microstructure and phase transformations.

Wire and Arc Additive Manufacturing (WAAM) is one of the modern methods of fabrication parts by arc welding under shielding gas. In this research, the thin-wall of austenitic stainless steel 316L was fabricated via WAAM based on inter-pulse current; accordingly, a thin-wall was fabricated in 25-layers using two different strategies with a reciprocating torch movement pattern. Considering the equivalent chromium and nickel content in the Scheffler diagram, it was predicted that the microstructure solidification was done in the austenitic-ferritic (AF) state. Microstructural examination by optical microscopy and X-ray diffraction confirmed the presence of austenite matrix phase alongside ferrite dendrites (about 5%). The tensile test results showed that samples extracted in the vertical direction with an average tensile strength of 454 MPa had about 12% higher strain rates than horizontal samples with a tensile strength of 436 MPa. Also, examination of fine and coarse indentations on the fracture surface of tensile test specimens by scanning electron microscopy showed that the fracture of the specimens was of the ductile type. The hardness of the fabricated thin-wall was measured in the range of 200 to 265 Vickers with an average of 234 Vickers.