Tavoosi M, Arjmand S. The Formation of Al3Ti Intermetallic compound at the junction interface of Titanium-Aluminum diffusional Coupling by Means of Diffusional Annealing Process. Journal of Advanced Materials in Engineering (Esteghlal) 2018; 37 (1) :37-44
URL: http://jame.iut.ac.ir/article-1-865-en.html
Department of Materials Engineering, Malek-Ashtar University of Technology (MUT), Shahin-Shahr, Isfahan, Iran. , ma.tavoosi@gmail.com
Abstract:   (7011 Views)

In this study, the formation of the Al3Ti intermetallic compound at the junction interface of aluminum-titanium was investigated during deposition and annealing. The results illustrated that during the deposition process, one thin layer of Ti3Al2 intermetallic compound was created at the junction interface. During the annealing at 550 °C, this layer was transformed to the  Al3Ti intermetallic phase and the layer growth occurred. By performing annealing at higher temperatures, the growth rate of Al3Ti intermetallic layer was increased; at the same time, the formation of Kirkendall cavities and  coupling in the cavities and fragmentation of diffusional coupling from the junction with aluminum were observed

Full-Text [PDF 646 kb]   (1264 Downloads)    
Type of Study: Research | Subject: Advanced Synthesis and production processes
Received: 2017/01/8 | Accepted: 2017/12/4 | Published: 2018/05/30

Add your comments about this article : Your username or Email:
CAPTCHA

Send email to the article author


© 2024 CC BY-NC 4.0 | Journal of Advanced Materials in Engineering (Esteghlal)

Designed & Developed by : Yektaweb