Tavakoli dehaghi S, Darvishi S, Nemati S, Kharaziha M. Preparation and Characterization of PDMS-SiO2-CuO Nanocomposite Coating on Stainless Steel and Its Super-hydrophobicity Property. Journal of Advanced Materials in Engineering (Esteghlal) 2018; 37 (3) :1-12
URL: http://jame.iut.ac.ir/article-1-901-en.html
URL: http://jame.iut.ac.ir/article-1-901-en.html
1. Department of Material Engineering, Isfahan University of Technology, Isfahan, 83111-84151, Iran. , sh.tavakoli73@yahoo.com
Abstract: (9965 Views)
Abstract: With the advances in the development of biomaterials for tissue replacement, the attention of scientists has been focused on the improvement of clinical implant properties. In this regard, despite the appropriate properties of the stainless steel, the application of stainless steel as implants has been limited due to the weak corrosion resistivity. The purpose of this paper was preparation and characterization of hydrophobic polydimethylsiloxane (PDMS)-SiO2-CuO nanocomposite coating on the 316L stainless steel surface. The 316L stainless steel was coated by SiO2 nanoparticles (20 wt. %), CuO nanoparticles (0.5, 1 and 2 wt. %) and biocompatible PDMS. In this research, x-ray diffraction (XRD) and scanning electron microscopy (SEM) were applied to characterize the coating. Moreover, the roughness and water contact angle of the coatings consisting of various amounts of CuO nanopowder were estimated. Finally, the effects of various amounts of the CuO nanopowder on the corrosion resistivity of nanocomposite coatings were investigated. XRD patterns confirmed the presence of crystalline CuO nanoparticles on the substrate. Due to the non-crystalline nature of silica nanoparticles and the semi-crystalline PDMS polymer, no peak confirming the presence of these phases was detected on the XRD pattern of the nanocomposite coating. SEM images showed the formation of a lotus leaf-like layer on the surface of the nanocomposite coating containing 1 and 2 wt. % CuO. Moreover, water contact angle evolution revealed that while contact angle was 81 degree without CuO nanoparticles, it was enhanced to 146 degree in the presence of 1 wt. % CuO. Moreover, the corrosion study showed the nanocomposite containing 2 wt.% CuO had the best corrosion resistance, the corrosion current density of 2.1E-7 A.cm-2, and the corrosion potential of 0.22 V.
Type of Study: Research |
Subject:
Biomaterials
Received: 2017/04/25 | Accepted: 2018/04/9 | Published: 2018/12/15
Received: 2017/04/25 | Accepted: 2018/04/9 | Published: 2018/12/15
Send email to the article author