saydi I, dehmolaei R, ranjbar K. Microstructural study of Ti/3YSZ interface in NI 105/Ni/Nb/Ti/3YSZ diffusion bonding. JWSTI 2022; 8 (1) :59-66
URL: http://jwsti.iut.ac.ir/article-1-399-en.html
Microstructural study of Ti/3YSZ interface in NI 105/Ni/Nb/Ti/3YSZ diffusion bonding
I. Saydi1 , R. Dehmolaei * 2, Kh. Ranjbar1
1- Department of Materials Science & Engineering, Faculty of Engineering, Shahid Chamran University of Ahvaz, Ahvaz, Iran.
2- Department of Materials Science & Engineering, Faculty of Engineering, Shahid Chamran University of Ahvaz, Ahvaz, Iran. , dehmolaei@scu.ac.ir
Abstract:   (2582 Views)
In this research, the diffusion bonding of the stabilized zirconia ceramic and Nimonic 105 superalloy using Ti/Nb/Ni multi-interlayer was carried out. Joint was performed using the plasma spark technique in a vacuum atmosphere and at different temperatures and times. The microstructure of the different joint zones was studied using optical and FESEM microscopes equipped with an EDS analyzer. The results showed that the critical region is Ti/3YSZ interface and in all conditions diffusion bonding in Ti/Nb, Nb/Ni, and Ni/NI 105 interfaces were done. Microstructural observations showed that in the Ti/3YSZ interface at all temperature and time conditions, the connection of two separate regions including Ti3O and (Zr, Ti)2O was formed due to the difference in the diffusion depth of Ti, Zr, and O elements and with increasing temperature and time, the thickness of these regions increased. Microstructural studies showed that the bond at 900 ℃  and 30 minutes did not have any cracks and discontinuities and due to the better diffusion of atoms, a suitable reaction layer was formed. Microhardness observations and EDS analyses confirmed that the Ti3O reaction layer is the weakest zine.
Keywords: Diffusion bonding, NI 105 superalloy, Zirconia stabilized ceramic, reaction layer
Full-Text [PDF 3386 kb]   (644 Downloads)    
Type of Study: Research | Subject: Special
Add your comments about this article : Your username or Email:
CAPTCHA
Send email to the article author

Rights and permissions
Creative Commons License This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.

© 2024 CC BY-NC 4.0 | Journal of Welding Science and Technology of Iran

Designed & Developed by : Yektaweb